Specification of Gasket Klingersil C-4243 Non Asbestos
Material based gaskets on organic fibres bound with NBR.Universal material gasket for general applications
Gasket material for liquids and gases at lower pressure and temperatures.Good chemical resistance to water and oil.
Klinger Hot and Cold Compression Test Method The Klinger Hot Compression Test
was developed by Klinger as a method to test the load bearing capabilities of gasket materials under hot
and cold conditions.In contrast to the BS 7531 and DIN 52913 tests, the Klinger
Compression test maintains a constant stress gasket throughout the entire test. This subjects the gasket to
more severe conditions.The thickness decrease is measured at ambient temperature of
23 ° C after applying the gasket load.This simulates assembly.Temperatures up to 300 ° C are then applied and the additional
the thickness reduction is measured. This simulates the first start up phase.
Typical values
Compressibility of ASTM F 36 J% 8
Recovery ASTM F 36 J min% 55
Stress relaxation DIN 52913 50 MPa, 16 h / 175 ° C MPa 24
Klinger cold / hot compression, thickness decrease at 23 ° C% 10
50 MPa thickness decreases at 200 ° C% 25
Tightness acc. to DIN 3535/6 mg / s x m <0.1
Thickness increase of ASTM F 146 oil JRM 903: 5 h / 150 ° C% 5
fuel B: 5 h / 20 ° C% 7
Density 9 / CM2 1.75
Dimensions of the standard sheets
Sizes: 1000 x 1500 mm, 2000 x 1500 mm.
Thicknesses: 0.5mm, 1.0mm, 1.5mm,2.0 mm, 3.0 mm;
other thicknesses and sizes on request.
Tolerances:thickness ± 10%, length ± 50 mm,width ± 50 mm